Harwell琥珀色3042劑量計(jì),

用于測(cè)量輻射劑量的Harwell琥珀色3042劑量計(jì)

1、材料：?jiǎn)闻晟?/span>3042劑量計(jì)由一塊聚甲基丙烯酸甲酯板材制作。

2、尺寸：30mm×11mm。厚度3±0.55mm

3、測(cè)量重復(fù)性：同批劑量計(jì)，在不均勻度小于±1%的輻照?qǐng)鲋型瑫r(shí)輻照，劑量范圍在1-10kGy用603nm波長(zhǎng)測(cè)量，劑量范圍在10-30kGy用651nm波長(zhǎng)測(cè)量，其吸光率測(cè)量的變異系數(shù)小于2.5%。

4、校準(zhǔn)能力：在校準(zhǔn)范圍內(nèi)，所有吸光率測(cè)量數(shù)據(jù)的平均值與使用zui小二乘擬合的四階多項(xiàng)式的數(shù)據(jù)相比，誤差在3%以內(nèi)。

5、溯源性：Harwell劑量計(jì)的校準(zhǔn)，溯源到英國(guó)國(guó)家物理實(shí)驗(yàn)室吸收劑量標(biāo)準(zhǔn)。

與英國(guó)國(guó)家物理實(shí)驗(yàn)室相互比較來(lái)驗(yàn)證每批劑量計(jì)的校準(zhǔn)性能。

6、保質(zhì)期：從發(fā)售日期起10年內(nèi)。

7、包裝：用聚酯/鋁箔/聚酯/聚乙烯材料制成的帶有標(biāo)簽的小袋密封包裝，每箱1000片。

Harwell Amber 3042

Harwell Amber 3042 Dosimeters

Amber 3042 are made from radiation-sensitive poly-methylmethacrylate （pmma） in the form of optically transparent pieces individually sealed in laminate sachets. They darken when irradiated, and the radiation-induced darkening, accuray measurable by means of a spectrophotometer, is a function of the radiation dose absorbed.

Dose Range

Amber 3042 has a functional dose range of 1 kGy to 30 kGy which makes it idea for low dose irradiation processes.

Material

The Amber 3042 is made from single batches of cast sheets of poly-methylmethacrylate （pmma）

Dimensions

Harwell Dosimeters then cut the sheets down into plaques of 30mm x 11mm with a thickness of 3mm （+/- 0.55mm）

Packaging

After * inspection the dosimeters are packaged into sealed sachets made of polyester/aluminium foil/polyester/polyethylene laminate. With each sachet being labeled with a unique bar coded label.

Packed 1,000 per carton.

（Packing to defined AQL's checked to BS6001 （ISO 2859-1）, single normal inspection, level II.）

Measurment reproducibility

Coefficient of variation of specific absorbance measurements on sets of dosimeters for the batch, simltaneously irradiated together, in a gamma radiation field uniform within +/- 1%, is 2.5% over the entire calibrated range, 1 to 30 kGy.

Calibration quality

Over the calibrated range, all mean specific absorbance data points thus obtained are within 3% of a fourth-order polynomial least-squares fit to the data.